An Analytical investigation of a failed 1120 Aluminium wire.

Simple item page
dc.creatorLoto, C. A.
dc.date2005-01
dc.date.accessioned2025-03-06T12:57:25Z
dc.descriptiona.n alytical investigation was performed on an - 120 aluminum wire which failed under stress test. ~.canning electron microscopy (SEM) examination ''nd the energy depressive spectrometer (EDS) nalysis were the major analytical methods of 1m.vestigation used. The failure mode of the alloy was found to be that of brittle failure interspersed · with ductile failure. The brittle failure results from he second phase particles contained within the luminium matrix which rendered the structure in . J):l .. -/1' ~ . . hif(region -weak and hence susceptible to failure . ,~:~ ABSTRACT a.n analytical investigation was performed on an - 120 aluminum wire which failed under stress test. ~.canning electron microscopy (SEM) examination ''nd the energy depressive spectrometer (EDS) nalysis were the major analytical methods of 1m.vestigation used. The failure mode of the alloy was found to be that of brittle failure interspersed · ith ductile failure. The brittle failure results from he second phase particles contained within the luminum matrix which rendered the structure in . J):l .. -/1' ~ . . hif(region -weak and hence susceptible to failure . ,~:~ , ... . . nder stress tests., ... . . nder stress tests.
dc.formatapplication/pdf
dc.identifierhttp://eprints.covenantuniversity.edu.ng/1297/
dc.identifier.urihttp://itsupport.cu.edu.ng:4000/handle/123456789/29656
dc.languageen
dc.subjectTJ Mechanical engineering and machinery
dc.titleAn Analytical investigation of a failed 1120 Aluminium wire.
dc.typeArticle

Files

Original bundle

Now showing 1 - 1 of 1
No Thumbnail Available
Name:
AN ANALYTICAL INVESTIGATION Of A fAILED 1120 ALUMINIUM WIRE.pdf
Size:
2 MB
Format:
Adobe Portable Document Format
Download

Collections

EPrint