Corrosion of Aluminum Alloy Metal Matrix Composites in Neutral Chloride Solutions

Simple item page
dc.creatorLoto, R. T., Adeleke, Adeyinka
dc.date2016-07
dc.date.accessioned2025-03-29T18:03:03Z
dc.descriptionThe electrochemical behavior of UNS A0332.00S, UNS A0332.20S, UNS A0359.00S, and UNS A0359.20S aluminum alloys were studied in NaCl media through weight loss, potentiodynamic, and cyclic polarization techniques. UNS A0332.20S and UNS A0359.20S were reinforced with SiC, 20% by volume while the other two samples were not reinforced. Scanning electron microscopy and energy dispersive spectroscopy were used to analyze the role of intermetallic phases in both the corroded and non-corroded aluminum alloy samples. Results showed that unreinforced alloys have lower corrosion rates compared to the reinforced alloys. Pits on the reinforced alloys were significantly more numerous, shallower, and widespread than on the monolithic alloys. Al/ SiC interface particles and intermetallic phases were observed to form at the mouth of the pits especially in alloys reinforced with SiC particles which might have contributed significantly to the weakening of regions where localized corrosion occurs. The result shows that intermetallic phases may directly influence the corrosion behavior of the aluminum alloys
dc.formatapplication/pdf
dc.identifierhttp://eprints.covenantuniversity.edu.ng/7311/
dc.identifier.urihttps://repository.covenantuniversity.edu.ng/handle/123456789/36645
dc.languageen
dc.publisherASM International
dc.subjectT Technology (General), TJ Mechanical engineering and machinery
dc.titleCorrosion of Aluminum Alloy Metal Matrix Composites in Neutral Chloride Solutions
dc.typeArticle

Files

Original bundle

Now showing 1 - 1 of 1
No Thumbnail Available
Name:
Corrosion of Aluminum Alloy Metal Matrix Composites in Neutral Chloride Solutions.pdf
Size:
2.18 MB
Format:
Adobe Portable Document Format
Download

Collections

EPrint