Evaluation of the influence of alumina nano-particle size and weight composition on the corrosion resistance of monolithic AA1070 aluminium
No Thumbnail Available
Date
Authors
Journal Title
Journal ISSN
Volume Title
Publisher
Elsevier
Abstract
Description
Corrosion resistance of AA1070 aluminium alloy (AA1070) was compared to AA1070 reinforced with alumina
at weight composition (wt. %) of 5% and 10%, and grain size of 150 nm and 600 nm.
Potentiodynamic polarization and open circuit potential analysis were employed in 0.0125 M H2SO4,
3.5% NaCl and 0.0125 M H2SO4-3.5% NaCl solutions. Data showed 0.0125 M H2SO4-3.5% NaCl solution
was the most deleterious with peak corrosion rate value of 6.682 mm/y while 3.5% NaCl solution was
the weakest with peak value of 0.084 mm/y. AA1070 at 5% (wt. %) and 150 nm particle size generally displayed
the highest corrosion rate with values between 0.084 and 6.682 mm/y. However, visible decrease
in corrosion rate occurred with increase in alumina weight fraction and particle size due to growth of the
protective oxide on the composite and reduction of discontinuities to minimal values between 0.031 and
2.192 mm/y at 10% alumina weight fraction and 600 nm particle size. Cathodic and anodic reaction mechanisms
significantly differs with respect to the electrolyte. Anodic reaction mechanism appeared under
activation control in the sulphate-chloride and chloride solution, compared to cathodic reaction mechanism
in the sulphate and sulphate-chloride solutions. Significant anodic degradation reaction was prevalent
on the anodic polarization plot in the sulphate solution. Plots from open circuit potential analysis
shows the composites and monolithic Al were the most thermodynamically stable in H2SO4 solution.
In the sulphate-chloride solution, significant potential transients coupled with high corrosion tendency
are conspicuous. The plot showed chaotic thermodynamic behaviour active passive transition behaviour
of the passive film.